朗盛激光焊接PBT Pocan B3235LT玻纤增强30%
PBT, 30 % glass fibers, injection molding, improved laser-transparency, NIR-laser transparent coloring (black)
Density (23°C) | 1.52 | g/cm³ | ISO 1183 |
Apparent (Bulk) Density | 0.70 | g/cm³ | ISO 60 |
Melt Volume-Flow Rate (MVR) (270°C/2.16 kg) | 20 | cm³/10min | ISO 1133 |
Molding Shrinkage 2 | ISO 294-4 | ||
2.00 mm | 0.050 | % | |
Across Flow : 2.00 mm |
| % | |
Flow : 2.00 mm | 0.30 | % |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 10000 | MPa | ISO 527-2/1 |
Tensile Stress (Break, 23°C) | 140 | MPa | ISO 527-2/5 |
Tensile Strain (Break, 23°C) | 2.8 | % | ISO 527-2/5 |
Flexural Modulus 3 (23°C) | 9500 | MPa | ISO 178/A |
Flexural Stress 3 (23°C) | 225 | MPa | ISO 178/A |
Flexural Strain at Flexural Strength 4 (23°C) | 3.2 | % | ISO 178/A |
Impact | Nominal Value | Unit | Test Method |
Charpy Unnotched Impact Strength (23°C) | 62 | kJ/m² | ISO 179/1eU |
Unnotched Izod Impact Strength (23°C) | 54 | kJ/m² | ISO 180/1U |
朗盛激光焊接PBT Pocan B3235LT玻纤增强30%