经销德国朗盛激光焊接PA6DurethanB31SKH30LT

Density (23°C)

1.13

--

g/cm³

Apparent (Bulk) Density

0.60

--

g/cm³

Molding Shrinkage

Across Flow : 120°C, 2.00 mm 2

0.20

--

%

Across Flow : 270°C, 2.00 mm 3

1.1

--

%

Flow : 120°C, 2.00 mm 2

0.20

--

%

Flow : 270°C, 2.00 mm 3

1.0

--

%

Water Absorption

Saturation, 23°C

10

--

%

Equilibrium, 23°C, 50% RH

3.0

--

%

Dry

Conditioned

Unit

Test Method

Ball Indentation Hardness

150

55.0

MPa

Dry

Conditioned

Unit

Test Method

Tensile Modulus (23°C)

3500

1000

MPa

Tensile Stress (Yield, 23°C)

80.0

45.0

MPa

Tensile Strain (Yield, 23°C)

4.0

20

%

Nominal Tensile Strain at Break (23°C)

10

> 50

%

Flexural Modulus 4 (23°C)

2900

900

MPa

Flexural Stress 4

23°C

115

35.0

MPa

3.5% Strain, 23°C

100

30.0

MPa

Flexural Strain at Flexural Strength 5 (23°C)

6.5

7.0

%