代理朗盛PA66 Durethan AKV25H3.0LT激光焊接级
PA 66, 25% glass fibers, injection molding, heat-aging stabilized, NIR-laser transparent coloring (black)
Property | Test Condition | Unit | Standard | |||
d.a.m. | cond. | |||||
Rheological properties | ||||||
C | Molding shrinkage, parallel | 60x60x2; 290 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.5 | |
C | Molding shrinkage, transverse | 60x60x2; 290 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 1.1 | |
Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.1 | ||
Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.1 | ||
Mechanical properties (23 °C/50 % r. h.) | ||||||
C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 8400 | 6000 |
C | Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 160 | 115 |
C | Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 3.0 | 6.0 |
C | Charpy impact strength | 23 °C | kJ/m² | ISO 179-1eU | 60 | 80 |
C | Charpy impact strength | -30 °C | kJ/m² | ISO 179-1eU | 50 | 50 |
C | Charpy notched impact strength | 23 °C | kJ/m² | ISO 179-1eA | 10 | 12 |
C | Charpy notched impact strength | -30 °C | kJ/m² | ISO 179-1eA | <10 | <10 |
Charpy notched impact strength | -40 °C | kJ/m² | ISO 179-1eA | <10 | <10 | |
Izod impact strength | 23 °C | kJ/m² | ISO 180-1U | 50 | ||
Izod notched impact strength | -30 °C | kJ/m² | ISO 180-1A | <10 | <10 | |
Izod notched impact strength | -40 °C | kJ/m² | ISO 180-1A | <10 | <10 | |
Flexural modulus | 2 mm/min | MPa | ISO 178-A | 7500 | 5000 | |
Flexural strength | 2 mm/min | MPa | ISO 178-A | 240 | 170 | |
Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 4.5 | 7.0 | |
Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | 220 | 145 |
代理朗盛PA66 Durethan AKV25H3.0LT激光焊接级