代理13玻纤PA66NILAMIDA3J10GF13耐低温冲击

Density (23°C)

1.20

g/cm³

Molding Shrinkage

Across Flow : 23°C

0.80

%

Flow : 23°C

0.50

%

Water Absorption

24 hr, 23°C

1.0

%

Saturation, 23°C

6.0

%

Nominal Value

Unit

Test Method

Tensile Modulus (23°C)

3500

MPa

Tensile Stress (Yield, 23°C)

90.0

MPa

Tensile Strain (Break, 23°C)

4.0

%

Nominal Value

Unit

Test Method

Charpy Notched Impact Strength (23°C)

13

kJ/m²

Notched Izod Impact Strength (23°C)

12

kJ/m²

Nominal Value

Unit

Test Method

Heat Deflection Temperature (1.8 MPa, Unannealed)

238

°C

Continuous Use Temperature 3

95.0

°C

Ball Pressure Test

125°C

Pass

165°C

Pass

Nominal Value

Unit

Test Method

Surface Resistivity 4

1.0E+12

ohms

Volume Resistivity (23°C)

1.0E+15

ohms·cm

Comparative Tracking Index (3.20 mm, Solution A)

500

V