天津供应帝斯曼K224-G6可承受-30°C跌落试验DSM尼龙6,成本效益高的解决方案(无需防腐蚀涂层)。
帝斯曼PA6 Akulon K224-G6 产品物性:
Physical | Dry | Conditioned | Unit | Test Method |
Density | 1.35 | -- | g/cm³ | ISO 1183 |
Melt Volume-Flow Rate (MVR) (240°C/2.16 kg) | 6.40 | -- | cm³/10min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 0.90 | -- | % | |
Flow | 0.30 | -- | % | |
Water Absorption (Saturation, 23°C) | 6.3 | -- | % | ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) | 1.9 | -- | % | ISO 62 |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 9500 | 6000 | MPa | ISO 527-2 |
Tensile Stress (Break) | 180 | 110 | MPa | ISO 527-2 |
Tensile Strain (Break) | 3.5 | 7.0 | % | ISO 527-2 |
Flexural Modulus | 8600 | -- | MPa | ISO 178 |
Flexural Stress | 235 | -- | MPa | ISO 178 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 11 | 11 | kJ/m² | |
23°C | 12 | 25 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 75 | 75 | kJ/m² | |
23°C | 90 | 110 | kJ/m² | |
Hardness | Dry | Conditioned | Unit | Test Method |
Shore Hardness (Shore D, 15 sec) | 85 | -- | ISO 868 | |
Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature (0.45 MPa, Unannealed) | 220 | -- | °C | ISO 75-2/B |
Heat Deflection Temperature (1.8 MPa, Unannealed) | 207 | -- | °C | ISO 75-2/A |
Vicat Softening Temperature | 216 | -- | °C | ISO 306/B50 |
Melting Temperature 2 | 220 | -- | °C | ISO 11357-3 |
CLTE - Flow | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
CLTE - Transverse | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
Effective Thermal Diffusivity | 1.12E-7 | -- | m²/s | |
Electrical | Dry | Conditioned | Unit | Test Method |
Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Electric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
Relative Permittivity | IEC 60250 | |||
100 Hz | 3.50 | 20.0 | ||
1 MHz | 3.30 | 5.00 | ||
Dissipation Factor | IEC 60250 | |||
100 Hz | 5.0E-3 | 0.30 | ||
1 MHz | 0.015 | 0.12 | ||
Comparative Tracking Index | -- | 600 | V | IEC 60112 |
Flammability | Dry | Conditioned | Unit | Test Method |
Flammability Classification | IEC 60695-11-10, -20 | |||
0.75 mm | HB | -- | ||
1.5 mm | HB | -- | ||
Glow Wire Flammability Index | IEC 60695-2-12 | |||
1.5 mm | 700 | -- | °C | |
2.0 mm | 700 | -- | °C | |
Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
1.5 mm | 725 | -- | °C | |
2.0 mm | 725 | -- | °C | |
Fill Analysis | Dry | Conditioned | Unit | Test Method |
Melt Density | 1.15 | -- | g/cm³ | |
Melt Thermal Conductivity | 0.27 | -- | W/m/K | |
Specific Heat Capacity of Melt | 2110 | -- | J/kg/°C |