汉高汉高导电胶,黄山半导体材料汉高ABLESTIKJM7000导电胶

LOCTITE ABLESTIK JM 7000 die attach adhesive has been
formulated for use in high throughput die attach applications. This
material has been used successfully on rigid substrates with die sizes
up to 700 mils.
LOCTITE ABLESTIK JM 7000 has been approved by DESC and
Rome Laboratory for military products.

TYPICAL PROPERTIES OF UNCURED MATERIAL
Viscosity, HAAKE RV-20 Rotoviscometer, mPa·s (cP):
Cone 1º @ Shear rate 22 s
-1 9,000
Work Life @ 25°C, hours 8 to 16
Shelf Life @ -40°C (from date of manufacture), days 365
TYPICAL CURING PERFORMANCE
Cure Schedule
30 minutes @ 150°C
Suggested temperature cures are from 150 to 350ºC. For
applications requiring higher electrical conductivity, a cure cycle of 15
minutes @ 300ºC is recommended. Product properties will not be
reduced by subsequent post die attach thermal exposure, i.e.,
wirebond, and/or lid seal up to 370ºC.

TYPICAL PERFORMANCE OF CURED MATERIAL
Die Shear Strength:
2 X 2 mm Si die, kg-f,
cured 20 minutes @ 150ºC
Substrate DSS
Ag/Cu LF ≥5
Tensile Strength :
cured 30 minutes @ 300ºC, MPa
After Cure After 1000 TC'C"
>17 >17
Radius of Curvature:
Si die on Alumina, meters
cured 30 minutes @ 300ºC
Chip Size: ROC
15 x 15 mm > 5

哪里有卖JM7000导电胶的？
北京汉高代理
汉高代理导电胶
乐泰导电胶
国产化导电胶
代替H20E导电胶

汉高乐泰导电胶,杨浦厚膜汉高ABLESTIKJM7000导电胶

ablestik84-1A导电胶

LOCTITE/乐泰ICP3535M1导电粘合剂导电胶

光器件尾纤粘结乐泰FS245绝缘导热胶水

光器件尾纤粘结乐泰F123快速固化低应力耐冲击胶水

LOCTITE/乐泰非导电粘合剂84-3导电银胶

光器件尾纤粘结乐泰F131透明胶水

汉高乐泰Ablestik84-1LMISR4导电银胶北京导电胶