汉高乐泰导电胶,鹤壁半导体材料汉高ABLESTIKJM7000导电胶

LOCTITE ABLESTIK JM 7000 die attach adhesive has been
formulated for use in high throughput die attach applications. This
material has been used successfully on rigid substrates with die sizes
up to 700 mils.
LOCTITE ABLESTIK JM 7000 has been approved by DESC and
Rome Laboratory for military products.

TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties
Coefficient of Thermal Expansion, :
Below Tg, ppm/°C 33
Glass Transition Temperature (Tg) by TMA, °C 240
Bulk Thermal Conductivity, W/(m-K):
@ 90°C 1.1
@ 165°C 1.0
Tensile Modulus, DMTA :
Cured 30 minutes @ 300ºC N/mm² 10,000
(psi) (1,450,377)
Extractable Ionic Content, @ 100°C:
Chloride (Cl-) <10
Sodium (Na+) <15
Potassium (K+) <15
Decomposition (in N2):
TGA analysis @ 10ºC/ minute ramp from 25 to 400
ºC
@ 340ºC, % 0.2
@ 400ºC, % 0.3
Electrical Properties
Sample cured 30 minutes @ 300ºC
Volume Resistivity, ohm-cm ≤0.01

TYPICAL PERFORMANCE OF CURED MATERIAL
Die Shear Strength:
2 X 2 mm Si die, kg-f,
cured 20 minutes @ 150ºC
Substrate DSS
Ag/Cu LF ≥5
Tensile Strength :
cured 30 minutes @ 300ºC, MPa
After Cure After 1000 TC'C"
>17 >17
Radius of Curvature:
Si die on Alumina, meters
cured 30 minutes @ 300ºC
Chip Size: ROC
15 x 15 mm > 5

汉高乐泰导电胶,杨浦厚膜汉高ABLESTIKJM7000导电胶

ablestik84-1A导电胶

LOCTITE/乐泰ICP3535M1导电粘合剂导电胶

光器件尾纤粘结乐泰FS245绝缘导热胶水

光器件尾纤粘结乐泰F123快速固化低应力耐冲击胶水

LOCTITE/乐泰非导电粘合剂84-3导电银胶

光器件尾纤粘结乐泰F131透明胶水

汉高乐泰Ablestik84-1LMISR4导电银胶北京导电胶