经销美国奥升德(首诺)玻矿低翘曲PA66 Vydyne R860
Vydyne R860 BK02可成功应用于各种注塑工程应用。典型零件包括汽车夹子、散热器罩、风扇和后视镜支架;电气连接器、外壳和线轴;以及工业应用,如齿轮、轴承壳、盖和外壳。
Density | 1.47 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow : 23°C, 2.00 mm | 0.80 | -- | % | |
Flow : 23°C, 2.00 mm | 0.25 | -- | % | |
Water Absorption | ISO 62 | |||
24 hr, 23°C | 0.60 | -- | % | |
Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus (23°C) | 10000 | 5900 | MPa | ISO 527-2 |
Tensile Stress (Break, 23°C) | 120 | 90.0 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 2.5 | 2.8 | % | ISO 527-2 |
Flexural Modulus (23°C) | 9000 | 4500 | MPa | ISO 178 |
Flexural Stress (23°C) | 190 | 97.0 | MPa | ISO 178 |
Poisson's Ratio | 0.40 | -- | ISO 527-2 | |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179 | |||
-30°C | 3.8 | 6.0 | kJ/m² | |
23°C | 4.4 | 10 | kJ/m² |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 230 | -- | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/A |
Melting Temperature | 255 | -- | °C | ISO 11357-3 |
CLTE | ISO 11359-2 | |||
Flow : 23 to 55°C, 2.00 mm | 2.4E-4 | -- | cm/cm/°C | |
Transverse : 23 to 55°C, 2.00 mm | 6.9E-4 | -- | cm/cm/°C |
PA66优点
1、具高抗张强度;2、耐韧、耐冲击性特优;3、自润性、耐磨性佳;4、低温特性佳;5、具自熄性;
PA66用途
广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器:连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车: 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件:椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输