原厂原包东丽玻纤增强高耐热PA66 AMILAN CM3006G-15
Amilan® CM3006G-15 is a Polyamide 66 (Nylon 66) product filled with 15% glass fiber.
Density (23°C) | 1.26 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage 2 | Internal Method | |||
Across Flow : 3.00 mm | 1.0 to 1.4 | -- | % | |
Flow : 3.00 mm | 0.70 to 1.0 | -- | % |
Rockwell Hardness | ISO 2039-2 | |||
M-Scale, 23°C | 95 | -- | ||
R-Scale, 23°C | 120 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Stress | ISO 527-2 | |||
-40°C | 155 | 145 | MPa | |
23°C | 110 | 90.0 | MPa | |
80°C | 65.0 | 50.0 | MPa |
Charpy Notched Impact Strength(23°C) | 6.0 | -- | kJ/m² | ISO 179 |
Charpy Unnotched Impact Strength(23°C) | 30 | -- | kJ/m² | ISO 179 |
Melting Temperature | 265 | -- | °C | DSC |
CLTE - Flow | 4.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
Specific Heat | 2000 | -- | J/kg/°C | |
Thermal Conductivity | 0.36 | -- | W/m/K |
防静电PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。
导电尼龙66：具有良好的耐磨性、耐热性、耐油性及耐化学药品性，还大大降低了原材料的吸水率和收缩率,具有优良的尺寸稳定性及的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制，适用于从100到1012欧姆/平方(ohms/sq)的表面电阻范围，可用于注塑及挤出等成型。有很多金属和涂装的优点:零件重量较轻，较易处理，运输成本较低。它们的装配简便，制造成本较低，并且较不会受到撞凹，割损和刮伤。为了标识或美观目的，一些材料可被预先染色，避免费时且昂贵的两次着色加工。
原厂原包东丽玻纤增强高耐热PA66 AMILAN CM3006G-15
- 玻纤增强高耐热PA66,日本东丽PA66
- 工程起重机械
- 广东深圳
- 金龙
玻纤增强高耐热PA66信息
-
代理日本东丽30玻纤PA66AMILANCM3001G-30¥ 37 -
2020年能不能拍卖黄花梨半月桌¥ 1000000 -
外卖APP外卖小程序跑腿系统定制开发面议 -
推荐泰安外pe内环氧防腐钢管厂家价格DN指导¥ 128 -
经销东丽热稳定30GFPA66AMILANCM3006G-30¥ 38.8 -
批发日本东丽45玻纤增强PA66AMILANCM3001G-45¥ 39.5