原包沙伯基础PBT/PC XENOY X6125抗冲
比重 | 1.24 g/cc | 1.24 g/cc | ASTM D 792 |
密度 | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
平衡吸湿 | 0.080 % | 0.080 % | 23°C / 50% RH; ISO 62 |
饱和吸水率 | 0.13 % @Temperature 23.0 °C | 0.13 % @Temperature 73.4 °F | ISO 62 |
线性成型收缩率,Flow | 0.0165 - 0.018 cm/cm @Thickness 3.20 mm | 0.0165 - 0.018 in/in @Thickness 0.126 in | SABIC Method |
熔体流动速率 | 17 g/10 min @Load 1.20 kg, Temperature 266 °C | 17 g/10 min @Load 2.65 lb, Temperature 511 °F | ASTM D 1238 |
28 g/10 min @Load 5.00 kg, Temperature 265 °C | 28 g/10 min @Load 11.0 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
简支梁缺口冲击强度 | 7.50 J/cm² @Temperature 23.0 °C | 35.7 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
冲击试验 | 59.0 J @Temperature 23.0 °C | 43.5 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线形热膨胀系数 - 流动 | 88.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 48.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
88.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 48.9 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
载荷下热变形温度(1.8 MPa) | 57.0 °C | 135 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
64.0 °C @Thickness 3.20 mm | 147 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
维卡软化温度 | 130 °C | 266 °F | Rate B/50; ASTM D 1525 |
132 °C | 270 °F | Rate B/50; ISO 306 | |
135 °C | 275 °F | Rate B/120; ISO 306 |
原包沙伯基础PBT/PC XENOY X6125抗冲