经销安科罗60%玻纤热稳定PA66 AKROMID A3GF601
Density (23°C) | 1.71 | -- | g/cm³ | ISO 1183 |
Spiral Flow 1 | 53.0 | -- | cm | Internal Method |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 0.40 to 0.60 | -- | % | |
Flow | 0.10 to 0.30 | -- | % | |
Water Absorption (Saturation, 23°C) | 3.2 to 3.7 | -- | % | ISO 62 |
Humidity Absorption - 62% RH(70°C) | 1.0 to 1.2 | -- | % | ISO 1110 |
Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness (H 961/30) | 330 | -- | MPa | ISO 2039-1 |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 20500 | 15800 | MPa | ISO 527-2/1 |
Tensile Stress (Break) | 260 | 190 | MPa | ISO 527-2/5 |
Tensile Strain (Break) | 2.0 | 2.5 | % | ISO 527-2/5 |
Flexural Modulus 2 | 19800 | -- | MPa | ISO 178 |
Flexural Stress 2 | 400 | -- | MPa | ISO 178 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 19 | -- | kJ/m² | |
23°C | 19 | 22 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 97 | -- | kJ/m² | |
23°C | 85 | 95 | kJ/m² |
Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 260 | -- | °C | ISO 75-2/A |
8.0 MPa, Unannealed | 235 | -- | °C | ISO 75-2/C |
Melting Temperature 3 | 262 | -- | °C | DIN EN 11357-1 |
CLTE | ISO 11359-2 | |||
Flow : 23 to 80°C | 1.2E-5 | -- | cm/cm/°C | |
Transverse : 23 to 80°C | 8.2E-5 | -- | cm/cm/°C |
PA66特性
1、具有优良的耐磨性、自润滑性,机械强度较高。但吸水性较大,因而尺寸稳定性较差
2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性,其程度主要取决于材料的组成、壁厚以及环境条件。
3、在产品设计时,一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性,经常加入各种各样的改性剂。玻璃就是常见的添加剂,有时为了提高抗冲击性还加入合成橡胶,如EPDM和SBR等。PA66的粘性较低,因此流动性很好(但不如PA6)。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。
4、PA66的收缩率在1%~2%之间,加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性,但对酸和其它一些氯化剂的抵抗力较弱。
经销安科罗60%玻纤热稳定PA66 AKROMID A3GF601