ISO | dry / cond | Unit | Test Standard |
Density | 1230 / - | kg/m³ | ISO 1183 |
Molding shrinkage, parallel | 0.6 | % | ISO 294-4, 2577 |
Molding shrinkage, normal | 0.8 | % | ISO 294-4, 2577 |
Water absorption, 23°C-sat | 6.5 / * | % | ISO 62 |
Humidity absorption, 23°C/50%RH | 1.2 / * | % | ISO 62 |
Tensile modulus | 5700 / - | MPa | ISO 527-2/1A |
Tensile stress at break, 5mm/min | 115 / - | MPa | ISO 527-2/1A |
Tensile strain at break, 5mm/min | 2.4 / - | % | ISO 527-2/1A |
Flexural modulus, 23°C | 4400 / - | MPa | ISO 178 |
Flexural stress at max. force | 160 / - | MPa | ISO 178 |
Charpy impact strength, 23°C | 35 / - | kJ/m² | ISO 179/1eU |
Izod impact notched, 23°C | 4.5 / - | kJ/m² | ISO 180/1A |
DTUL at 1.8 MPa | 245 / * | °C | ISO 75-1, -2 |
DTUL at 0.45 MPa | 250 / * | °C | ISO 75-1, -2 |
Flammability @0.8mm nom. thickn. | HB / * | class | UL 94 |
Flammability @3.2mm nom. thickn. | HB / * | class | UL 94 |
Other | dry / cond | Unit | Test Standard |
Continuous service temperature | 140 / * | °C | DIN/IEC 60216-1 |
防静电PA,导电PA,加纤防火PA,防火PA,抗紫外线耐候PA,高温挤出级PA。
导电尼龙66:具有良好的耐磨性、耐热性、耐油性及耐化学药品性,还大大降低了原材料的吸水率和收缩率,具有优良的尺寸稳定性及的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制,适用于从100到1012欧姆/平方(ohms/sq)的表面电阻范围,可用于注塑及挤出等成型。有很多金属和涂装的优点:零件重量较轻,较易处理,运输成本较低。它们的装配简便,制造成本较低,并且较不会受到撞凹,割损和刮伤。为了标识或美观目的,一些材料可被预先染色,避免费时且昂贵的两次着色加工。