原包意大利拉提PA6 Laticonther 62 GR/70石墨导热级
Density | 1.76 | g/cm³ | ISO 1183 |
Molding Shrinkage 3 | ISO 294-4 | ||
Across Flow : 2.00 mm | 0.25 to 0.45 | % | |
Flow : 2.00 mm | 0.25 to 0.40 | % |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 22000 | MPa | ISO 527-2/1 |
Tensile Stress (Break, 23°C) | 60.0 | MPa | ISO 527-2/5 |
Tensile Strain (Break, 23°C) | 0.30 | % | ISO 527-2/5 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eU |
Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
Vicat Softening Temperature | 200 | °C | ISO 306/B50 |
CLTE - Flow (30 to 100°C) | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
Thermal Conductivity 4 | 15 | W/m/K | ASTM E1461 |
Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 10 | ohms | ASTM D257 |
Volume Resistivity | 1.0E+2 | ohms·cm | ASTM D257 |
原包意大利拉提PA6 Laticonther 62 GR/70石墨导热级