安科罗30%GF高抗冲PA66 AKROMID A3GF307S3
Density (23°C) | 1.33 | -- | g/cm³ | ISO 1183 |
Humidity Absorption - 62% RH(70°C) | 2.1 | -- | % | ISO 1110 |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 9000 | 5000 | MPa | ISO 527-2/1 |
Tensile Stress (Break) | 165 | 100 | MPa | ISO 527-2/5 |
Tensile Strain (Break) | 3.6 | 7.2 | % | ISO 527-2/5 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 18 | -- | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | 90 | -- | kJ/m² | ISO 179/1eU |
Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 235 | -- | °C | ISO 75-2/A |
Melting Temperature 1 | 262 | -- | °C | DIN EN 11357-1 |
Additional Information | Dry | Conditioned | Unit | Test Method |
Reinforcement Content | 30 | -- | % | ISO 1172 |
PA66(聚酰胺66或尼龙66),同PA6相比,PA66更广泛应用于汽车工业、仪器壳体以及其它需要有抗冲击性和高强度要求的产品。广泛用于制造机械、汽车、化学与电气装置的零件,如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。
安科罗30%GF高抗冲PA66 AKROMID A3GF307S3