经销安科罗30%GF高抗冲PA66 AKROMID A3GF30S1

Mechanical Properties	Metric	English	Comments

Density	1.35 g/cc	0.0488 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ISO 294-4

Tensile Strength at Break	180 MPa	26100 psi	5 [mm/min]; ISO 527-2
Elongation at Break	3.5 %	3.5 %	5 [mm/min]; ISO 527-2
Tensile Modulus	9.00 GPa	1310 ksi	1 [mm/min]; ISO 527-2
Flexural Strength	255 MPa	37000 psi	2 [mm/min]; ISO 178
Flexural Modulus	8.00 GPa	1160 ksi	2 [mm/min]; ISO 178
Charpy Impact Unnotched	8.00 J/cm² @Temperature -30.0 °C	38.1 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	9.00 J/cm² @Temperature 23.0 °C	42.8 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	1.30 J/cm² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	262 °C	504 °F	DSC, 10K/min; DIN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi)	250 °C	482 °F	ISO 75/A
Deflection Temperature at 8.0 MPa	210 °C	410 °F	ISO 75/C
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

PA66特性

1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差

2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。

3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。

4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。